^ A magnifying glass (10X magnification) must be used to identify impact marks that may be less than 1 mm in diameter.

NOTE:

A lead, or crack from an impact point can run to the edge of the glass and appear to be a low stress crack starting from the glass outside edge.

Compound crack beginning or ending at the edge of the glass

This type of crack is always caused by impact to the glass. The point of impact is located where the crack "branches out".

Cracks that are only in the middle of the glass

This type of crack does not begin or end at the edge of the glass.

^ These cracks are always caused by an impact to the glass and are not covered under warranty.

2. Cracks Due to Scratch In Glass Surface

2) How to determine if glass damage is due to a scratch in the glass surface.

Cracks from a scratch in the glass surface