NOTICE:  There is a marked decrease in the panel strength if heated over the heating temperature limit.

d. CHARACTERISTICS OF ALUMINUM ALLOY

1. If the base metal of aluminum alloy is left untreated, it will naturally develop an oxide film that will protect against corrosion. As a result,

an anti-rust agent does not need to be used even when aluminum alloy is exposed to heat during shrinking.

2. Aluminum alloy conducts heat very well so a wide area will become heated when heat is applied to one area.

3. Aluminum alloy does not become magnetized.

e. PRECAUTIONS WHEN CONDUCTING REPAIRS

1. If aluminum comes into contact with another type of metal (especially steel), galvanic corrosion will cause the base metal to corrode. If

tools used to repair steel panels are not cleaned before they are used on aluminum alloy surfaces, the tools will leave behind steel particles
and corrode the base metal.
Therefore make sure to completely clean off iron particles on the surface of tools if using them to repair steel parts before use, or prepare a
separate set of tools (hammers, dollies, chisels, air sander, carbon electrode, etc.) for use on aluminum alloys only.

HINT:  Galvanic corrosion is rusting that is created by a potential difference between two metals that is produced when they come in to
contact together. This phenomenon occurs with any type of metal, and the aluminum causes the corrosion when the base metal surfaces of
aluminum and steel are put together.

2. An oxide film forms on an aluminum alloy within a matter of minutes when the base metal is exposed to the air.

This oxide film has a negative effect on putty and paint adhesion, so it is important to immediately treat the base metal after sanding and
degreasing.

3. Aluminum is brittle and easily develops work hardening and cracks. Heating aluminum when restoring a deformed portion improves

workability and prevents work hardening and cracking so it is an effective method when repairing. However, heating at the optimal heating
temperature provides the very best results and any increase in temperature above this will result in a corresponding decrease in strength.
(There is a marked decrease in strength if the optimal heating temperature is exceeded.)

f.

CHOOSING THE REPAIR METHOD

g. THE WORK PROCEDURE OF EACH REPAIR METHOD

-

Repair by Pulling.