Description and Operation The manufacturer's instructions must always be followed when dealing with any materials! The information given in the following text is data which is independent of the manufacturer, and it should only used as an indication. Adhesive sealants Adhesive sealants are permanently elastic, long-lived, can be painted and accept filler. Application: Sealing of visible and normal seams. Can be over-painted with 2-component paint, primer and fillers after having dried throughout. Contamination can be removed using cleaner and thinner. 1-component PUR adhesive sealant Note: - Hardens using oxygen from the air. For that reason, it must only be stripped after it has completely dried through.
2-component MS polymer adhesive sealant 2-component MS polymer adhesive sealant is free of isocyanate, solvent and silicones and can be spot-welded. MS polymer adhesive sealant Can be over painted with water-based paints. Suitable for spraying and brushing to obtain a composition true to the original. MS polymer adhesive sealant is free of isocyanate, solvent and silicones and can be spot-welded. Underbody protection Underbody protection products are immune to abrasion, permanently elastic, adhere well and are suitable for a true to original texture. Underbody protection based on solvent Application: - Underbody protection for visible areas.
Properties: - Can be over-painted, also with 2-component paint.
- Can be colored with a proportion of up to 40% paint.
Note: - Contamination can be removed using cleaner and thinner.
Water based underbody protection Can be over-painted with water based paint. Can be colored with water based paint. Contamination can be removed using water. Application | Water based underbody protection | Use | Underbody protection for visible areas | Spray viscosity | ready to use | Spray gun | Suction beaker HVLP gun 3 - 4 mm | Spray pressure | 4 - 6 bar | Layer thickness | 500 - 1000 µm | Drying | approx. 6 hours at 20°C | | approx. 45 - 60 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | Application | Water based underbody protection | Use | Isolation primer for peroxide marks, bloomed old paintwork and thermoplastics. | Spray viscosity | Thin as necessary with distilled water | Spray gun | HVLP gun 1.9 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | 40 - 50 µm | Drying | approx. 2 hours at 20°C | | approx. 30 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | Paint additives Application | Sanding test color | Use | To test sanding results | Spray gun | HVLP 1.7 - 1.9 mm | Spray pressure | 2.0 bar | Layer thickness | Spray drifted | Application | Fixer additive | Use | Converts solid top coat into two layer solid; multicolor painting | Spray viscosity | 18 - 20 secs at 20°C | Spray gun | HVLP 1.2 - 1.3 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | max. 30 µm | Coat application | Wet on wet | Ventilation time | approx. 15 - 30 minutes | Maintain maximum layer thickness without fail. Must always next be overpainted with clear lacquer. Application | Drying accelerator | Use | Accelerates drying with only minimal reduction in working life | Working life | approx. 5 hours at 20°C | Spray gun | HVLP 1.2 - 1.3 mm | Spray pressure | 2.0 bar | Layer thickness | 50 - 70 µm | Drying | approx. 6 hours at 20°C | | approx. 25 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | Cannot be used in all paints, read the manufacturer's instructions. Particularly suitable for partial painting. Application | Elastifier additive in primer material | Use | Elastifies the complete paint structure on plastics. | Addition | Up to 25% | Spray gun | HVLP 1.7 - 1.9 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | 50 µm | Drying | approx. 4 hours at 20°C | | approx. 40 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | Application | Elastifier additive in top coat | Use | Elastifies the complete paint structure on plastics. | Addition | Up to 25% | Spray gun | HVLP 1.7 - 1.9 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | 50 - 60 µm | Drying | approx. 16 hours at 20°C | | approx. 45 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | Application | Matting additive in solid paint | Use | Elastifies the complete paint structure on plastics. | Semi-gloss addition | Up to 25% in the paint without hardener and thinner | Silk gloss addition | Up to 35% in the paint without hardener and thinner | Silk matt addition | Up to 45% in the paint without hardener and thinner | Spray gun | HVLP 1.2 - 1.3 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | 50 - 70 µm | Drying | approx. 8 hours at 20°C | | approx. 30 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | CAUTION:Do not dry using infrared. Application | Matting additive in clear lacquer | Use | Elastifies the complete paint structure on plastics. | Semi-gloss addition | Up to 25% in the paint without hardener and thinner | Silk gloss addition | Up to 35% in the paint without hardener and thinner | Silk matt addition | Up to 45% in the paint without hardener and thinner | Spray gun | HVLP 1.2 - 1.3 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | 50 - 70 µm | Drying | approx. 8 hours at 20°C | | approx. 30 minutes at 60°C | Note: - When mixing, first put in the matting additive, then the hardener and thinners.
- Stir immediately after adding the matting additive.
- Do not store after addition of the matting additive, storage will change the degree of gloss.
- Also suitable for use on plastics without addition of elastifier additive.
Application | Matting paste | Use | Matts, elasticizes and gives structure to solid paint and clear lacquer during painting of bumpers or hard plastic. | Addition | 1:1 or 2:1 depending on manufacturer in solid paint without hardener or thinners. | Spray gun | HVLP 1.2 - 1.3 mm | Spray pressure | 2.0 - 3.0 bar | Layer thickness | 50 - 70 µm | Drying | approx. 6 - 10 hours at 20°C | | approx. 30 minutes at 60°C | | Short wavelength infrared approx. 8 minutes | | Medium wavelength infrared approx. 10 - 15 minutes | Note: - The paint must not be filtered.
Application | Anti-silicone additive | Use | Prevents silicone craters | Addition | 2% to maximum 5% | Note: - Only add away from the paint cabin and immediately remove contaminated cloths.
- If anti-silicone additive is used in the first coat, then it must be used in the following coats, and in at least the same proportions.
Additive materials Variety of adhesive tapes For profile, fine and large area masking work. Properties: - Withstands heat.
- Withstands water-based paint.
- Accepts paint.
- Easily removed without leaving adhesive residues.
Masking film. For masking of large areas on vehicles. Properties: - Accepts 2-component and water-based paints.
- Withstands heat.
- Withstands water spray and condensation.
- Withstands solvent.
- Easily cut.
- Environmentally friendly and can be recycled.
Polishing materials. Polishing means microfine sanding. For this reason, polishes must only contain abrasives, and no silicones. During polishing repair, a good shine is achieved through the step-by-step use of polishes, starting with a highly abrasive polish and ending with a polish having very slight abrasive action. Polishes are available in graduations from coarse to fine. Abrasives Please refer to the "Tools" chapter for information on abrasives. |