Porsche Workshop Service and Repair Manuals

-

Polyester products, sanded

-

Cleaned sheet steel, sanded

-

Factory primer and KTL, sanded

-

Aluminum and galvanized base surfaces must be pre-primed with Standox(R) Etching Adhesion Primer

-

Please note base surface pre-treatment instructions:
->  S 5.1
->  S 6.1
->  S 9.2.2

NOTE:

-

Raw material base: Acrylic polyurethane, corrosion inhibition pigments

-

Flash point: 24° C/75.2° F

-

Spec. weight: 1.55 g/cm3

-

Solid content: 70.3% weight/47.7% vol.

-

Theoretical yield as wet-on-wet filler: 13.9 m2/ltr. with a dry coat thickness of 30 microns

-

Theoretical yield: 5.2 m2/ltr. with a dry coat thickness of 80 microns

-

Clean equipment after use with cleaning thinner

VOC value:

-

460 g/l

NOTE:

-

VOC-compliant when used as a sanding filler with up to 8% thinner added.

-

Use with Standox(R) 2K Plasticizer (new) on primed plastics.

WARNING:  2K paints react with moisture. All work equipment, mixing vessels, etc. must therefore be completely water-free.

S 9.5.2.1 Application as a wet-on-wet filler