Base surfaces:

-

Hardened paintwork, sanded

-

Polyester products, sanded

-

Cleaned sheet steel, sanded

-

Factory primer and KTL, sanded

-

Aluminum and galvanized base surfaces

-

Fiber-reinforced plastic

-

Please note base surface pre-treatment instructions:
->  S 5.1
->  S 6.1
->  S 9.2.2

NOTE:

-

Raw material base: Epoxy resin, corrosion inhibition pigments

-

Flash point: 28° C/82.4° F

-

Spec. weight: 1.6 g/cm3

-

Solid content: 73.8% weight/52.4% vol.

-

Theoretical yield: 5.6 m2/ltr. with a dry coat thickness of 75 microns

-

Clean equipment with cleaning thinner

VOC value:

-

420 g/l

NOTE:

-

Do not use Standox(R) EP Primer Surfacer on acid primer.

S 9.5.4.1 Application as a wet-on-wet filler

S 9.5.4.2 Working with sanding filler