Porsche Workshop Service and Repair Manuals

Base surfaces:

-

Hardened paintwork, sanded

-

Polyester products, sanded

-

Cleaned sheet steel, sanded

-

Factory primer and KTL, sanded

-

Aluminum and galvanized base surfaces must be pre-primed with Standox(R) Etching Adhesion Primer

-

Please note base surface pre-treatment instructions:
->  S 5.1
->  S 9.2.2

NOTE:

-

Raw material base: Acrylic polyurethane, corrosion inhibition pigments

-

Flash point: 26° C/78.8° F

-

Spec. weight: 1.41 g/cm3

-

Solid content: 61.3% weight/38.8% vol.

-

Theoretical yield: 7.5 m2/ltr. with a dry coat thickness of 50 microns

-

Theoretical yield: 4.2 m2/ltr. with a dry coat thickness of 90 microns

-

Clean equipment after use with cleaning thinner

VOC value:

-

545 g/l

WARNING:  2K paints react with moisture. All work equipment, mixing vessels, etc. must therefore be completely water-free.

S 9.6.1.1 Processing