Description:

-

Conventional basecoat for double-layer solid, metallic and pearl-effect paint finishes

Properties:

-

Optimum color accuracy

-

Excellent filling properties

-

Good coverage

-

Suitable for spot painting

Base surfaces:

-

Hardened paintwork, sanded

-

Standox(R) 2K Nonstop Primer Filler

-

Standox(R) 2K Universal Filler

-

Standohyd(R) 1K Primer Surfacer

-

Please note base surface pre-treatment instructions:
->  S 5.1
->  S 6.1
->  S 9.2.2

NOTE:

-

Raw material base: Physically-drying special resin

-

Flash point: 25° C/77° F

-

Spec. weight: 0.93-1.06 g/cm3

-

Solid content: 22.0-37.2% weight/17.7-22.0% vol.

-

Theoretical yield: 7.1-8.8 m2/ltr. with a dry coat thickness of 25 microns

-

In higher layers (multiple paint layers) of 40 microns or higher, mix Standox(R) Basecoat with 20% Standox(R) 2K Hardener MS 25-40 /
Standox(R) 2K Hardener MS X 5-25 or 15% Standox(R) 2K Hardener HS 25-40 and set with 40% Standox(R) Thinner MSB 15-25. Allow a
correspondingly longer time to dry.

-

Standox(R) Basecoat can be masked after 45-60 min./20° C or after oven-drying. Hardened Standox(R) Basecoat should only be masked
following oven-drying.

-

Clean equipment after use with cleaning thinner

VOC value:

-

460-719 g/l

S 9.7.1.1 Processing