TPO FLEXIBLE PLASTIC (FRONT AND REAR BUMPER COVERS)

Thermoplastic olefin (TPO) is a soft thermoplastic used for exterior applications where flexible characteristics are required in order to absorb minor
impacts without sustaining damage. Special attention must be given to materials as well as procedures when repairing TPO. Among these are the need
for adhesion promoters and epoxy based repair materials.

Level 1

Refer to refinish procedures for detailed instructions.

Level 2

Cosmetic damage, minor scratches and gouges.

1. Clean repair area with soap and water followed by grease and wax remover. Wipe dry.
2. Use a two or three inch #50 grade disc to enlarge the damaged area.
3. With a random orbital sander fitted with a #180 grade disc, remove the paint film from the surrounding area to be filled. The repair material should

not overlap the painted surface.

4. Apply a double wet coat of 3M(R) Polyolefin Adhesion Promoter-#5907 to entire exposed area.
5. Mix 3M(R) Flexible Parts Repair Material-#5900 according to instructions and apply to the repair area with a squeegee or plastic spreader. Build

the material slightly higher than the undamaged surface. Allow repair material to cure 20-30 minutes at 16 degrees C to 27 degrees C (60
degrees F to 80 degrees F).

6. When material is cured, shape repair material with a curved tooth body file. Sand with grade 180A Stikit gold disc followed by grade 240A Stikit

gold disc.

7. If low areas or pin holes remain, first apply 3M(R) Polyolefin Adhesion Promoter #5907 or equivalent, then mix and spread additional repair

material as in step 5.

8. Apply one coat of PPG DPX-800 Polypropelene Primer over the exposed bare substrate. Allow to dry 10-15 minutes.
9. Apply primer surfacer with flex as outlined in "Flexible Parts Refinishing" and block sand.

LEVEL 3

Damage in the form of small cracks or punctures.

Due to the flexible characteristics of TPO it is necessary to reinforce all cracks and punctures which penetrated the substrate with the following
recommended procedure. This process is also useful for repairing attaching surfaces which are cracked or broken away.