Most windshield damage that occurs due to impact is easily identified as shown above.

Cracks can spread and become larger from the original strike point or crush mark due to:

^ Thermal stresses caused by temperature fluctuation

^ External physical stresses, such as hand touch, wind force, or vehicle vibration during driving (pot holes)

A lead, or crack from one of the star cracked impact points can run to the edge of the glass and appear to be a low stress crack starting from the glass
outside edge.

Single crack beginning or ending at the edge of the glass

Single cracks must be inspected along the entire crack for impact marks.

^ If any impact mark is found anywhere along the crack, it indicates the damage occurred from an object striking the windshield. This is not covered

under warranty.