^ A magnifying glass (10X magnification) must be used to identify impact marks that may be less than 1 mm in diameter.

NOTE:

A lead, or crack from an impact point can run to the edge of the glass and appear to be a low stress crack starting from the glass outside edge.

Compound crack beginning or ending at the edge of the glass

This type of crack is always caused by impact to the glass. The point of impact is located where the crack "branches out".

Cracks that are only in the middle of the glass

This type of crack does not begin or end at the edge of the glass.

^ These cracks are always caused by an impact to the glass and are not covered under warranty.

2) How to determine if glass damage is due to a scratch in the glass surface.

Cracks from a scratch in the glass surface

Glass is produced by fusing together various raw materials such as silica, soda ash, and limestone, and has a hardness of 5 to 6 on the Mohs scale (for
reference, a diamond has a hardness of 10 on the same scale).

Since earth and sand can contain substances harder than that of glass, glass can be easily scratched by:

^ Fine sand particles

^ Hard metal

^ Rubbing action of contaminated wiper rubbers, or sand partials caught between the wiper and the glass, especially when operating the wipers in a dry