Porsche Workshop Service and Repair Manuals

hologram.

This is particularly visible in dark and shiny double-layer shades. Different clear lacquers also have different properties in terms of their hologram
sensitivity.

Holograms are only visible in direct sunlight or when lit by halogen lamps, but not under neon lighting.

Polishing procedure for largely hologram-free painted surfaces:

1. Clean the painted surface with a 3M-2010 micro-fiber cloth soaked in Glasurit(R) Cleaner 700-1.
2. Polish the painted surface to a high gloss using an eccentric polishing machine, a 3M-09551 polishing disc and 3M-82878 polish.

NOTE:
-

For relatively old painted surfaces, it may be necessary to use a more aggressive polish or a more abrasive polishing sponge.

-

Do not exert any great pressure on the painted surface. If you do, it will heat up and you will end up with an even worse polishing result.

-

It is important to use an eccentric machine to prevent any directional micro-scratches.

3. Clean the painted surface with a 3M-2010 micro-fiber cloth soaked in Glasurit(R) Cleaner 700-1.

NOTE:  Always wipe in one direction (linear to the vehicle's longitudinal axis) when cleaning the painted surface.

4. Shine a halogen lamp over the painted surface and check for holograms.
5. If holograms are still visible, repeat the polishing procedure.

G 8.9.1.1 Materials and tools

See: Section G9/G9.1 - Sanding Products

G9.1 - Sanding Products

G 9.1 Sanding Products

G 9.1.1 General information

The sanding products sector has undergone a change in recent years. For improved standardization of sandpaper and its grain, the FEPA (Federation of
European sanding product manufacturers) has defined a new standard. Sandpapers that comply with this standard are identified by a >P< in front of their
grain specification.

The latest development is that sandpapers are being coated electrostatically. As a result, a very uniform alignment of the sanding product and spray is
achieved in an upward direction, and the sandpaper works more intensively.

Aluminum oxide or silicone carbine is used as the abrasive grain. Paper manufactured in accordance with the FEPA standard includes the sandpaper in
the P16 to P2000 grain range. Experience has shown that paper coated with aluminum oxide is more effective for sanding factory paint finishes,
hardened old paint finishes and other hard base surfaces.

G 9.1.1.1 Instructions for use

After sanding, all dust must be thoroughly cleaned from the areas. For dry-sanding, blow off dust using compressed air and polish off surface again with
an anti-dust cloth.

For wet-sanding, wash with pure water, rub well until dry (including edges and seams), and allow residual moisture long enough to dry off. If the area is
not cleaned well, the dust remaining on the surface can cause small blisters and adhesion problems.